Using Fly Ash And Bottom Ash Boiler Of Palm Oil Factories As Adsorbents For Adsorption Of Color In Artificial Liquid Waste
DOI:
https://doi.org/10.35335/mekintek.v11i2.15Kata Kunci:
Bottom Ash Oil Palm Boiler, Fly Ash Oil Palm Boiler, Fixed Bed Adsorption Column, Color, CodAbstrak
This study aims to determine the ability of battom ash and fly ash in adsorbing artificial wastewater dye (PtCo) and chemical oxygen demand (COD) with three variations of adsorbent used in adsorption column. This research begins with the process of washing, drying and sieving adsorbent. Then proceed with the activation process of adsorbent using HCl 1 M which is heated at 90 0C for 1 hour accompanied by stirring. The adsorption system used is continuous (column) with up-flow flow pattern and using the pump to provide pressure so that the influent can pass through the adsorbent contained in the column. The characteristic analysis of adsorbent was done on moisture content, ash content, and iodine absorption. The highest moisture content and ash content obtained were 0.6% with fly ash adsorbent before activation and 0.285% with fly ash adsorbent after activation. Compared with SNI 06-3730-95 has been appropriate, while the iodine drainage from bottom ash was 35.38 mg/g and fly ash of 50.76 mg/g and none meet SNI 06-3730- 95 of 750 mg/g. The highest efficiency results in dye and COD were found in adsorption column with fly ash adsorbent with color value of 96.96% and COD concentration of 83.26%, followed by stratified columns with combined adsorbent between battom ash and fly ash with color values of 53 , 93% and COD of 62.82%, and adsorbent by using battom ash efficiency of highest color value of 53.03% and COD of 71.08%. The highest adsorption capacity was obtained by using adsorption column with battom ash and fly ash (BF) adsorbent of 8.42 mg/g, followed by fly ash (FA) of 7.53 mg/g and battom ash (BA) of 7, 37 mg/g.
Referensi
Abdulbari, A. Ahmad.,dkk. 2006. Basic Dye Removal from Synthetic Wastewater by Adsorption on Palm Ash. University Science Malaysia; Malaysia.
Ahmad, Mohd. Rafatullah., Arniza Ghazali., Othman Sulaiman dan Rokiah Hashim., 2011. Oil Palm Biomass–Based Adsorbents For The Removal Of Water Pollutants AReview. Universiti Sains Malaysia; Penang.
Akbar, M. I., 2011. Pemanfaatan Arang Aktif Cangkang Kelapa Sawit Sebagai Adsorben Zat Warna pada Biodiesel. Skripsi Departemen Ilmu Kimia Fakultas Matematika dan Ilmu Pengetahuan Alam Institut Pertanian Bogor. Dipublikasi.
Altwai, Nurdeen M., Megat A. Megat Johari, Syed F. Saiyid Hashim., 2011. Influence of Calcination Temperature on Characteristics and Pozzolanic Activity of Palm Oil Waste Ash. Australian Journal of Basic and Applied Sciences, 5 (11). Halaman: 1010-1018.
AL-,Aoh H. A., M. JamilMaah., A.A.Ahmad., M. Radzi.2012. Isotherm and Kinetic Studies of 4-nitrophenol Adsorption by NaOH-Modified Palm Oil Fuel Ash.Journal of Purity, Utility Reaction and Environment 104-120.
Anjani, Dwi., 2015. Pembuatan Silika Gel Menggunakan Abu Kerak Boiler PT. Sriwijaya Palm Oil Indonesia Terhadap Pengaruh Konsentrasi Na2CO3 Sebagai Pelarut. Skripsi Politeknik Negeri; Sriwijaya.
Asyri, Fadhilla., Kartini Noor Hafni., dan A. Haris Simamora., 2015. Pengaruh Limbah Abu Pembakaran Biomassa Kelapa Sawit Terhadap Sifat-Sifat Fisika dan Mekanik High Impact Polystyrene. jurnal Teknik Kimia USU.
Abbas,Muhammad., Ahmad Zaini., Tee Yee Cher, Muaz Zakaria, Mohd. Johari Kamaruddin, Siti Hamidah Mohd. Setapar & Mohd. Azizi Che Yunus.,
Palm oil mill effluent sludge ash as adsorbent for methylene blue dye removal.Universiti Teknologi Malaysia; Penang.
Budiono, A., Suhartana, Gunawan., 2006. Pengaruh Aktivasi Arang Tempurung Kelapa dengan Asam Sulfat dan Asam Fosfat untuk Adsorpsi Fenol, Jurnal Kimia; Universitas Diponegoro.
Balittri, J. T.,2013. Kandungan Senyawa Kimia Pada Daun The (Cmellia Sinensis). Warta penelitian dan pengembangan tanaman industri.
Clair N. S., Perry, L. M., dan Gene, F. P., 2003. Chemistry for Environmental Engineering and Science. 5th edition. McGraw-Hill; New York.
Fadli, A., Komalasari, Roza, L., dan Maria, E., 2002. Penjerapan Fenol dengan Tandan Kosong Sawit (TKS) sebagai Adsorben. Prosiding Seminar Nasional Fundamental dan Aplikasi Teknik Kimia;Surabaya.
Febijanto, Irhan., 2010. Pemanfaatan Potensi Gas Metana di Pabrik Kelapa Sawit Sei Silau,PTPN 3, Sumatera Utara. J. Tek. Ling. Hal. 459- 474.
Farandia R. Y., Monita Olivia., Lita Darmayanti., 2015. Kinerja Beton High Volume POFA. Jurnal Program Studi Teknik Sipil Fakultas Teknik Universitas Riau; Pekanbaru.
Hadiwidodo, Mochtar., 2008. Penggunaan Abu Sekam Padi Sebagai Adsorben Dalam Pengolahan Air Limbah Yang Mengandung Logam Cu. Halaman :55-63.
Herlandien, Y. L., 2013, Pemanfaatan Arang Aktif sebagai Adsorban Logam Berat dalam Air Lindi di TPA Pakusari Jember. Skripsi Fakultas Matematika dan Ilmu Pengetahuan Alam; Universitas Jember.
Hudaya, Tedi., dan Wiratama G. P., 2016. Perancangan Kolom Adsorpsi Karbon Aktif untuk Pengolahan Limbah Kromium Heksavalen. Laporan Hibah Monopoli.Universitas Katolik Parahyangan. Bandung.
Idrus, R., Lapanporo, B, P., Putra, Y, S, 2013, Pengaruh Suhu Aktifasi Terhadap Kualitas Karbon Aktif BErbahan Dasar Tempurung Kelapa. Prisma Fisika. Halaman 50-51.
Irawan, Candra., Basri Dahlan.,Nawang Retno., 2015.Pengaruh Massa Adsorben, Lama Kontak Dan Aktivasi Adsorben Menggunakan HCl Terhadap Efektivitas Penurunan Logam Berat (Fe)Dengan Menggunakan Abu Layang Sebagai Adsorben. Jurnal Teknologi Terpadu. Hal 1-12.
Imla, Syafiqah., Hafizuddin Wan Yussof., Abdul Aziz Mohd Azoddein., Shivananda Chandraseagar., dan Faizal Wan Ishak., 2017. A Factorial Analysis Study on Removal of Mercury by Palm Oil Fuel Ash Adsorbent. Jurnal Faculty of Chemical Engineering & Natural Resources, Universiti Malaysia Pahang.Halaman: 1-6.
K. Maghanga, F. K. Segor, L. Etiégni & J. Lusweti., 2009. Electrocoagulation Method for Colour Removal In Tea Effluent: A Case Study Of Chemomi Tea Factory In Rift Valley, Kenya. Chemical Society of Ethiopia. Halaman: 371- 381.
Jamilatun, Siti., Intan Dwi Isparulita., Elza Novita Putri., 2014. Karakteristik Arang Aktif Dari Tempurung Kelapa Dengan Pengaktivasi H2SO4 Variasi Suhu dan Waktu. Jurnal Fakultas Teknologi Industri, Universitas Ahmad Dahlan; Yogyakarta.
Jannah., Miftahul., 2015. Pembuatan Silika Gel Dari Abu Cangkang Kelapa Sawit dan Fiber Kelapa Sawit PT. SPOI dengan Pengaruh Temperatur Ekstraksi. Skripsi Politeknik Negeri Sriwijaya; Palembang.
Laos, Landiana Etni., dan Arkilaus Selan., 2016. Pemanfaatan Kulit Singkong Sebagai Bahan Baku Karbon Aktif. Jurnal Ilmu Pendidikan Fisiku; Nusa Tenggara Timur. Halaman 32-36
Laos, Landiana.,Etni Masturi., Ian Yulianti., 2016. Pengaruh Suhu Aktivasi Terhadap Daya Serap Karbon Aktif Kulit Kemiri. Halaman: 1-6.
Metcalf & Eddy 1991. Wastewater Engineering Treatment, Disposal and Reuse. 3th Edition. MC. Graw- Hill. New York. America.
Mu’jizah, S., 2010, Pembuatan dan Karakterisasi karbon Aktif dari Biji Kelor (Moringa oleifera. Lamk) dengan NaCl sebagai Bahan Pengaktif. Skripsi Fakultas Sains dan Teknologi. Universitas Islam Negeri Maulana Malik Ibrahim; Malang.
Malakootian M., dan Fatehizadeh A., 2010. Color Removal From Water by Coagulation/Caustic Soda and Lime. Department of Environmental Health Engineering, School of Public Health, Kerman University of Medical Sciences, Kerman, Iran. Halaman: 1-6.
Muthawali, D. I., 2013. Analisa COD Dari Campuran Limbah Domestik dan Laboratorium di Balai Riset dan Standarisasi Industri Medan. Jurnal FMIPA Universitas Sumatera Utara. Halaman: 1-13.
M, Istifiarti., dan Alfan, P., 2016. Penurunan Ion Besi (Fe) dan Mangan (Mn) dalam Air dengan Serbuk Gergaji Kayu Kamper. Jurnal Teknik ITS. Halaman: 11- 16.
Nur T., Shim,W.G., dan Loganatahan, P.,2014. Nitrate removal using purolite A520E Ion Exchange Resin Bed Column Adsorption Modeling. International journal of Enviromental and science technology. Halaman: 1311-1320.
Pari, G., 2004. Kajian struktur arang aktif dari serbuk gergaji kayu sebagai adsorbe emisi formaldehida kayu lapis. disertasi. Bogor: Sekolah Pascasarjana, Institut Pertanian Bogor.
Patisarana, Grata., dan Mulfi Hazwi., 2012.Optimalisasi Efisiensi Termis Boiler Menggunakan Serabut Dan Cangkang Sawit Sebagai Bahan Bakar Jurnal Dinamis. Halaman: 16-26.
Putranto. A., dan Stephanie A., 2014. Pemodelan Perpindahan Massa Adsorpsi Zat Warna Pada Florisil dan Silica Gel dngan Homogeneous and
Prianti, E., Malino, B, A., dan Lapanporo, B,P., 2015. Pemanfaatan Abu Kerak Boiler Hasil Pembakaran Limbah Kelapa Sawit Sebagai Pengganti Parsial Pasir pada Pembuatan Beton. Positron.
Ruthven, D. M., 1984. Principle of Adsorption & Adsorption Process. John Wiley & Sons : New York,124-141.
Reynolds, T. D. dan Paul, A. R., 1996. Unit Operations and Processes in Environmental Engineering. Edisi kedua. PWS Publishing Company; USA.
Reza, Muhammad., Rahmi Karolina., dan Johannes Tarigan., 2014. Pengaruh Limbah Abu Boiler Dan Fly Ash Sebagai Bahan Pengganti Semen Dalam Campuran Beton. Universitas Sumtera Utara; Medan.
Standar Nasional Indonesia (SNI). 1995. Arang Aktif Teknis SNI 06-3730-1995. Jakarta: Dewan Standardisasi Nasional.
Sentosa, L.,2005. Kinerja Laboratorium Campuran Hot Rolled Asphalt dengan Abu Sawit sebagai Filler. Simposium VIII Forum Studi Transportasi Antar- Perguruan Tinggi. (FSTPT). Palembang; Universitas Sriwijaya.
Said, Muhammad., Arie Wagi Prawati., dan Eldis Murenda., 2008.Aktifasi Zeolit Alam Sebagai Adsorbent Pada Adsorpsi Larutan Iodium.Jurnal Teknik Kimia.
Suhendra, D., dan E. R. Gunawan.,2010. Pembuatan Arang Aktif Dari Batang Jagung Menggunakan Aktivator Asam Sulfat dan Penggunaannya Pada Penyerapan Ion Tembaga (II). Jurnal Universitas Mataram. Halaman: 22-26.
Setiaka,Juniawan., Dra Ita Ulfin, MSi., Nurul Widiastuti, Ph.D.,2011. Adsorpsi Ion Logam Cu(Ii) dalam Larutan Pada Abu Dasar Batubara Menggunakan Metode Kolom. Prosiding Skripsi Jurusan Kimia Fakultas Matematika dan Ilmu Pengetahuan Alam Institut Teknologi Sepuluh Nopember.
Siti, Jamilatun., Intan Dwi Isparulita., dan Elza Novita Putri., 2014. Karakteristik Arang Aktif Dari Tempurung Kelapa Dengan PengaktivasI H2SO4 Variasi Suhu dan Waktu. Fakultas Teknologi Industri, niversitas Ahmad Dahlan.Yogyakarta.
Suparma, Latif Budi., Tunggul W., Panggabean., Sandra Mude., 2014. Potensi Penggunaan Limbah Kelapa Sawit Sebagai Agregat Pengisi Pada Campuran Hot Rolled Sheet-Base. Jurnal Transportasi. Halaman:87-96.
Simarmata., 2017. Pengaruh Penggunaan Bottom Ash Kelapa Sawit dengan Aktivasi Fisik Terhadap Prestasi Mesin dan Emisi Gas Buang Sepeda Motor Bensin 4-Langkah. Skripsi Fakultas Teknik Universitas Lampung Bandar Lampung.
Triawan, Deni Agus., Nesbah Nesbah., dan Dyah Fitriani., 2017. Crude Palm Oil’s (CPO) Fly Ash As A Low-Cost Adsorben For Removal Of Methylen Blue (Mb) From Aqueous Solution.Jurnal Kimia Riset. Halaman 10-15.
Utama, Selvy., Hans Kristianto dan Arenst Andreas., 2016.Adsorpsi Ion Logam Kromium (Cr (Vi)) Menggunakan Karbon Aktif dari Bahan Baku Kulit Salak. Prosiding Seminar Nasional Teknik Kimia “Kejuangan”.Bandung. Halaman: 1-16.
Webar, W bend. M., 1972, “Adsorption in heterogenes Aqua in Sistem ”, Jaour AWWA.
Wibowo, Santiyo., Wasrin Syafii., & Gustan Pari., 2009. Karakteristik Arang Aktif Tempurung Biji Nyamplung (Calophyllum Inophyllum Linn). Balai Penelitian Kehutanan Aek Nauli, Kampus Kehutanan Terpadu Aek Nauli Sumatera Utara. Halaman: 1-19
W, Kusnanto Mukti., 2012., Penentuan Konsentrasi Permanganat (KMnO4). jurnal Jurusan Fisika, FMIPA Universitas Sebelas Maret; Surakarta.
Yulika, Jeni., 2010. Penjerapan Zat Warna Reaktif Cibacron Red Menggunakan Adsorben Sekam Padi. Skripsi Departemen Kimia Fakultas Matematika Dan Ilmu Pengetahuan Alam Institut Pertanian; Bogor.
Yelvi., dan Mukhli., 2013. Evaluasi Kinerja Campuran Beton Aspal Lapis Aus (AC- WC) Memakai Limbah Abu-CPO Sebagai Filler. Jurnal Rekayasa Sipil.
Zarina, Y.,A. M. MustafaAl Bakri1, H. Kamarudin1, I. Khairul Nizar and A. R. Rafiza., 2013. Review on the Various Ash From Palm Oil Waste as Geopolymer Material. Red, Adv, Master. Sci. 34; Universiti Malaysia Perlis (UniMAP). hal.37-43.
Unduhan
Diterbitkan
Cara Mengutip
Terbitan
Bagian
Lisensi
Hak Cipta (c) 2020 Juang Jaya Putra Telaumbanua
Artikel ini berlisensi Creative Commons Attribution-NonCommercial 4.0 International License.